Nanocrystal and surface alloy properties of bimetallic Gold-Platinum nanoparticles

Derrick Mott, Jin Luo, Andrew Smith, Peter N Njoki, Lingyan Wang and Chuan-Jian Zhong*

Author Affiliations

Department of Chemistry, State University of New York at Binghamton, Binghamton, New York, 13902, USA

For all author emails, please log on.

Nanoscale Research Letters 2006, 2:12-16  doi:10.1007/s11671-006-9022-8

Published: 30 November 2006

Abstract

We report on the correlation between the nanocrystal and surface alloy properties with the bimetallic composition of gold-platinum(AuPt) nanoparticles. The fundamental understanding of whether the AuPt nanocrystal core is alloyed or phase-segregated and how the surface binding properties are correlated with the nanoscale bimetallic properties is important not only for the exploitation of catalytic activity of the nanoscale bimetallic catalysts, but also to the general exploration of the surface or interfacial reactivities of bimetallic or multimetallic nanoparticles. The AuPt nanoparticles are shown to exhibit not only single-phase alloy character in the nanocrystal, but also bimetallic alloy property on the surface. The nanocrystal and surface alloy properties are directly correlated with the bimetallic composition. The FTIR probing of CO adsorption on the bimetallic nanoparticles supported on silica reveals that the surface binding sites are dependent on the bimetallic composition. The analysis of this dependence further led to the conclusion that the relative Au-atop and Pt-atop sites for the linear CO adsorption on the nanoparticle surface are not only correlated with the bimetallic composition, but also with the electronic effect as a result of the d-band shift of Pt in the bimetallic nanocrystals, which is the first demonstration of the nanoscale core-surface property correlation for the bimetallic nanoparticles over a wide range of bimetallic composition.

Keywords:
Gold-Platinum nanoparticles; Nanocrystal alloy; Surface binding sites; Bimetallic composition